Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 6, Article number: 18927 (2016 ) Cite this article Zirconium Oxide Nanoparticles
Recently, the defect-induced static magnetic behaviours of nanomaterials have been a cutting-edge issue in diluted magnetic semiconductor materials. However, the dynamic magnetic properties of nanomaterials are commonly ignored if their bulk counterparts are non-magnetic. In the present research, titanium nitride-carbon (TiN/C) nanocomposites were found to exhibit both static and dynamic magnetic properties that vary in the opposite trend. Moreover, novel unconventional electromagnetic resonance behaviour was demonstrated in TiN/C systems and their permeability and permittivity show similar trend. This is challenging for the traditional understanding of electromagnetism and makes it possible to achieve an appropriate balance between the permeability and permittivity simultaneously in a simple system. Hopefully, the results could provide some valuable clues to revealing the magnetism and electromagnetism of nanostructures.
Nanomaterials are drawing increased attention in recent years, since they usually possess many unique physical properties (mechanical, optical, electrical, magnetic properties and so on) when compared with their bulk counterparts1,2,3,4. Due to the high surface to volume ratio of nanostructured materials, various defects (e.g., vacancies, dislocations and dangling bonds) are usually inevitable, which would affect the physical properties of nanomaterials in unexpected way5. For example, since Coey et al. reported the unexpected d0 magnetism in a dielectric oxide in 2004, the defect-induced static magnetic properties of nanomaterials have been a cutting-edge issue in diluted magnetic semiconductors (DMSs) materials6,7. The unique magnetism of nanomaterials is attributed to a variety of structural defects, such as cation vacancies, oxygen vacancies and structural inhomogeneity, as verified by numerous studies on highly defective dilute magnetic oxides and nitrides7,8,9,10,11,12,13.
Recently, serious electromagnetic interference has been driving considerable efforts on the development of advanced microwave absorbing material (MAM). The microwave absorption properties are evaluated with the complex permeability (μr = μr′ + iμr″) and permittivity (εr = εr′ + iεr″). The real part is related to the stored electrical and magnetic energy within the medium while the imaginary part is related to the dissipation of electrical and magnetic energy and their ratios, the dielectric (tan δE = εr″/εr′) and magnetic dissipation factors (tan δM = μr″/μr′) provide a measure of how much power is lost versus how much is stored in a material14,15. Ideal MAM should possess not only strong electromagnetic loss ability but also a proper complementariness between the complex permeability and permittivity, so-called impedance match. Up to now, some significant breakthroughs have been achieved by integrating magnetic and dielectric components together16,17, or turning the inactive MAM into an exciting MAM18,19. However, few are currently available about the extraordinary electromagnetic behavior of nanostructures upon encountering with dynamic electromagnetic wave20. Especially, based on the classical relationship between static magnetic properties and dynamic permeability, it is accepted that only conventional magnetic compositions (such as Fe, Co, Ni, magnetic alloys and ferrites) are considered as the origin of the permeability behavior and the microwave magnetic loss of nanomaterials is not expected if their bulk counterparts are intrinsically non-magnetic or weak magnetic and the dissipation power is expectedly to be solely determined by dielectric loss20,21,22,23. In our very recent researches, we have found that though bulk titanium nitride (TiN) is non-magnetic, TiN nanostructures obtained with the assistance of defect engineering possess both evident static ferromagnetic and dynamic permeability properties24,25,26; and we preliminarily suppose that the composition and microstructure defects have profound effects on both the magnetic and electromagnetic properties. These results remind us to investigate whether there is any relationship between the defect-induced static and dynamic magnetic properties and whether there is any similar mechanism between the permeability and permittivity behaviors of nanomaterials, which remains untouched up to now.
Bearing those perspectives in mind, in the present research we adopt titanium nitride-carbon (TiN/C) nanocomposite as a simple example to investigate the magnetic and electromagnetic behaviours of nanostructured materials. TiN/C nanocomposite is focused on, because it is easy to create the non-stoichiometric solid solutions in the host materials (TiN) by replacing N with heteroatomic substitutions (C) of the similar atomic radius, thereby resulting in more defects. Systematic studies in relation to the composition, structure and defects were conducted, with the hope to acquire some insights into the magnetism and electromagnetism of nanostructured materials and achieve ideal absorption.
Figure 1a shows the X-ray diffraction (XRD) patterns of as-obtained samples. It can be seen that only tetragonal anatase TiO2 is obtained at 400 °C and rutile TiO2 coexistent with TiN powder is obtained at 700 °C. As the nitriding temperature rises to 900 °C and above, only pure face centered cubic TiN nanoparticles are obtained. As to the Raman spectrum of TiN, it has been evidenced that the scattering in the acoustic range is mainly determined by the vibrations of the heavy metal (Ti) ion vacancies (typically 150–350 cm−1) and light element (N) ion vacancies (typically 400–650 cm−1)27. As shown in Fig. 1b, the Raman peaks of T-900 correspond to anatase TiO2 but not TiN. The Raman features at 150 cm−1, 394 cm−1, 506 cm−1 and 627 cm−1 are attributed to the Raman-active modes of crystalline anatase TiO2 with symmetries of Eg, B1g, A1g and Eg, respectively28. Here, it should be noted that the Raman scattering signals of anatase TiO2 are very strong and there are some overlapped signals between anatase TiO2 and TiN. This is consistent with what is reported in Ref. 29; that is, even though there is a small amount of anatase TiO2 in the as-synthesized TiN samples, the O-Ti-N and Ti-N bonds do not contribute any new Raman band. In other words, though anatase TiO2 in sample T-900 could not be detected by XRD, there is still some residual O, due to inadequate degree of nitriding. Differing from T-900, sample T-1000 shows the basic Raman scattering signals of TiN and some typical characteristic peaks of anatase TiO2 (for example, the peak at 506 cm−1) disappear totally28, which means that more complete nitriding reaction occurs at 1000 °C24. Besides, both T-900 and T-1000 show D and G peaks of carbon at about 1333 cm−1 and 1590 cm−1, respectively, which directly proves that they contain carbon. The magnified XRD patterns of as-prepared T-900 and T-1000 are shown in Fig. 1c. It can be seen that the XRD peaks of T-1000 shift towards lower 2θ as compared with those of T-900, which means that T-1000 exhibits an increased lattice constant. This well corresponds to relevant mean plane (200) distance of standard TiN (JCPDS card: 38–1420; 0.2121 nm) as well as that of T-900 (0.2103 nm) and T-1000 (0.2109 nm). In combination with corresponding Raman scattering signals, we can reasonably speculate that the smaller lattice constants of T-900 and T-1000 as compared with those of the standard TiN might be attributed to the presence of substitutial oxygen atoms. Increasing nitriding temperature might result in a higher content of N to promote the occupation of more O positions by N atom and to form near-stoichiometric TiN, thereby leading to the increment of the lattice constant of TiN.
XRD patterns of T-400, T-700, T-900 and T-1000 (a), Raman spectra (b) and magnified XRD patterns at low 2θ (c) of T-900 and T-1000.
The transmission electron microscopic (TEM) images of the as-obtained samples are shown in supplementary Fig. S1. It can be seen that both T-900 and T-1000 appear as nanoparticles with an average size of about 20 nm. Figure 2 shows the high-resolution TEM (HRTEM) images taken randomly on sample T-900, which provides evidences to the presence of defects in as-produced TiN powders (such as lattice defects and dislocations in regions “I” and “II”). Considering that the TiN particles obtained under similar conditions without carbon exhibit good crystallinity in the grains and at the grain boundaries (shown in supplementary Fig. S1 in ref. 26), we could infer that the dissolving of a great deal of C and some residual O in association with inadequate nitriding are responsible for the generation of the defects in T-900, because C, N and O can exist as non-stoichiometric solid solution in TiN crystal. In comparison, T-1000 has a well-defined crystalline structure, which indicates that calcining NTA precursor at 1000 °C can well transform it into TiN crystal with good crystallinity. Moreover, the amorphous regions “III” and “IV” at the grain boundaries of T-900 and T-1000 might be assigned to the amorphous carbon and/or the amorphous TiN.
HRTEM images of T-900 (a) and T-1000 (b).
The frequency dependencies of the complex relative permittivity and permeability are shown in supplementary Fig. S2. It can be seen that samples T-400 and T-700 have very small εr′ and εr″ that remain almost constant of 0.5 and 0 in the whole frequency range of 2 ~ 18 GHz. Meanwhile, their μr΄ and μr″ values are nearly 1.0 and 0 in the whole frequency range. Therefore, their tan δE and tan δM values are ignorable at gigahertz frequency, as shown in Fig. 3. Differing from T-400 and T-700, both T-900 and T-1000 exhibit obvious complex relative permittivity and permeability. In combination with relevant XRD results, it could be concluded that the composition feature determines the naturally electromagnetic properties and the main electromagnetic active component in as-prepared nanocomposites is TiN rather than TiO2.
The frequency dependence of tan δE and tan δM of the paraffin composites filled with T-400, T-700, T-900 and T-1000.
Moreover, T-1000 has much higher εr′ and εr″ than T-900 in the whole frequency range and the tan δE value of T-1000 composite is higher than that of T-900 therein. The real relative complex permittivity (εr′) and the imaginary part (εr″) of relative complex permittivity represent the energy storage ability and loss ability, respectively. Thus, the high imaginary parts of the permittivity is propitious for possessing ideal dielectric loss ability (tan δE = εr″/εr′)30. According to the free electron theory, free electrons have distinct effect on the imaginary part of relative complex permittivity and ε″ ≈ 1/2 πε0 ρf, where ρ is the resistivity15. It could be speculated that the higher ε″ values of T-1000 at 2–18 GHz indicate a higher electrical conductivity with respect to T-900 and would result in the increase of dielectric loss. In combination with relevant XRD and Raman data, we can suppose that the improved crystallinity and elevated nitridation degree of TiN obtained at a higher calcining temperature account for the significantly increased conductivity and dielectric loss of T-1000. This is consistent with the work conducted by Vaz et al. in that the electrical resistivity of TiN films is mainly determined by its phase composition, microstructure and defects (dislocations, impurities and grain boundaries) and the high quality of TiN results in the increased conductivity31.
What should be emphasized is that both T-900 and T-1000 exhibit an anomalous μr″ and magnetic loss at 8 ~ 12 GHz, though both TiN and C are not among the traditional magnetic material candidates. Specifically, as-prepared T-900 displays exceptionally high tan δM (its maxima value is 0.60) even over most of conventional magnetic fillers such as carbon nanotubes/Fe3O4 (~0.34)32, zinc ferrite nanofiber (~0.27)33, mesoporous Fe3O4 aerogels (~0.28)34 and RGO/Co3O4 (~0.22)35. When compared to traditional microwave absorbing materials such as resistance radar-absorbing materials, dielectric absorbing materials and magnetic medium absorbent materials, the unexpected high tan δM of TiN/C nanocomposites is unique and worth special attention, which is contributive to improving the consumption of electromagnetic energy and to the coexistence of tan δE and tan δM thereby favoring electromagnetic wave absorption.
Figure 4 comparatively shows the frequency dependence of tan δM and tan δE of composites T-900 and T-1000. It is seen that the tan δE and tan δM of TiN/C nanocomposites not only vary with varying EM wave frequency in very similar manners, but also exhibit very similar dielectric and magnetic resonance peaks. For example, to T-900, the peaks of dielectric loss overlapped those of magnetic loss at 5.70 GHz, 7.45 GHz, 10.0 GHz and 13.9 GHz, respectively. To T-1000, the similar resonance electromagnetic peaks could be observed at 3.71 GHz, 4.95 GHz, 6.93 GHz, 9.20 GHz, 10.5 GHz, 14.2 GHz and 16.3 GHz, respectively. These results confound our traditional understanding of electromagnetism in solids. Because the permittivity and permeability represent two different types of vector states of the electromagnetic wave and they are connected to the energy stored/consumed in an electric field and a magnetic field, respectively. While considerable efforts have been paid theoretically and experimentally, the similar electromagnetic variation behavior of the permeability and permittivity has not been reported to date. Here, the anomalously electromagnetic resonances imply the similar electric/magnetic energy consumed mechanism and make is possible to achieve an appropriate balance between the permeability and permittivity simultaneously in a simple system.
The frequency dependence of dielectric loss (tan δE) and magnetic loss (tan δM) of paraffin-matrix composites filled with T-900 (a) and T-1000 (b).
Further, combining the corresponding Raman spectra of T-900 and T-1000 with their HRTEM images, we can infer that the electromagnetic losses attributed to the naturally physical properties of the absorbing materials and their structures and defects have profound effects on both the magnetic and dielectric loss. For example, the interfacial polarization and the associated relaxation could contribute to the electromagnetic loss, similar to what is observed in other composite system16. Besides, various defects can also serve as polarized centers and have a significant effect on the electromagnetic loss. Moreover, under the alternating electromagnetic field, the electrons arising from oxygen vacancies would migrate back and forth in response to both the electric field and the magnetic field, thus leading to lags of polarization and electromagnetic loss. The schematic diagram for possible microwave absorbing mechanism of TiN/C composites is shown in supplementary Fig. S3.
To further prove the dependence of the microwave absorption properties on the permittivity and permeability, we have calculated the reflection losses [RL (dB)] of the TiN/C composites according to the transmit line theory20. Figure 5 shows the two-dimensional reflection loss mapping plots of the paraffin composites filled with T-900 and T-1000 as functions of frequency and thickness of absorbers. It can be seen that the reflection loss of composite T-1000 is relatively poor (more than −10 dB between 2–18 GHz). This is possibly because composite T-1000 exhibits relatively high dielectric loss and low magnetic loss which counteract the EM matching principle and hinder the absorption of EM wave. In contrast, composite T-900 exhibits enhanced microwave absorption [<−10 dB] in very broad frequency ranges (2.0 ~ 8.8 GHz and 11.7 ~ 18.0 GHz) when its thickness is adjusted from 1 mm to 6 mm. Therefore, it is reasonable to deduce that such a significant enhancement of the microwave wave absorption of composite T-900 is a consequence of the high tan δM and the impedance match between tan δE and tan δM.
Two-dimensional plots showing frequency dependence of the RL of paraffin composites filled with (a) T-900 and (b) T-1000.
To further investigate the relationship between the static and dynamic magnetic properties, we measured the magnetization (M) versus applied magnetic field (H) curves of T-900 and T-1000 by SQUID at room temperature (298 K). As shown in Fig. 6a, both T-900 and T-1000 possess a distinct ferromagnetic hysteresis loop, corresponding to pronounced room-temperature ferromagnetism. Particularly, a higher nitridation temperature corresponds to an enhanced nitridation degree of NTA as well as an enhanced magnetic moment of as-prepared TiN/C nanocomposite, which is well consistent with what is reported on undoped TiN nanoparticles obtained under different nitriding duration24. As to T-900, though it exhibits ferromagnetic behavior with coercive field in a range of −1 kOe < H < 1 kOe, its magnetization at a higher magnetic field decreases in association with a negative slope, which indicates that T-900 exhibits diamagnetic properties36. As the magnetization measurement is a bulk effect, the diamagnetic signal might be due to the contributions from the contaminations and a small concentration of impurities below the detecting limits of XRD and Raman or the diamagnetic susceptibility of TiN1−xOx37. Moreover, we also investigated the dynamic magnetic properties of the paraffin-matrix composites filled with TiN nanoparticles without carbon, T-4 and T-24. To explain the differences between the tan δM of various paraffin-matrix composites filled with T-900, T-1000, T-4 and T-24, we demonstrate the corresponding frequency-tan δM curves in Fig. 6b. Firstly, the tan δM of the paraffin-matrix composites separately filled with T-4, T-900 and T-1000 changes with the frequency in similar manner, which might be governed by their similar composition feature and microstructure defects. Secondly, sample T-900 exhibits a larger dynamic permeability than un-doped TiN (T-4). Considering that the only difference between samples T-900 and T-4 is that the latter is obtained under similar conditions without carbon, we can stipulate that the incorporation of carbon is responsible for the improvement in the magnetic loss of TiN nanocrystallites. Thirdly, elevating nitridation degree corresponds to a decrease in the dynamic permeability of various samples (comparison between T-4 and T-24, or between T-900 and T-1000). Based on Snoek theory (μ*fr ∝ Ms), the permeability and the resonance frequency are proportional to the saturation magnetization38. Evidently, this theory is invalid in the present research and there is no straightforward dependence between the static magnetic properties and the dynamic magnetic properties of TiN/C nanocomposites. On the one hand, the evident microwave dynamic permeability could not be attributed to their weak static magnetic properties. On the other hand, the static and dynamic magnetic properties show the opposite trend, increasing nitridation degree refers to an enhanced static magnetic moment but a decreased dynamic permeability. Hopefully, this work could enlighten us to understand the intrinsic reasons for microwave absorption mechanism and to develop new absorbing materials with excellent microwave absorption performances. However, it should be noted that the exact mechanism is relatively complicated and requires further theoretical analysis.
Hysteresis loops of T-900 and T-1000 observed in a range of −5 kOe < H < 5 kOe at 298 K (a) and frequency dependence of magnetic loss (tan δM) of corresponding paraffin composites (b), the upper left inset in (a) shows the hysteresis loops of the two samples between −500 and 500 Oe.
Herein, we adopt titanium nitride-carbon (TiN/C) nanocomposite as a concrete example to investigate both the static and dynamic magnetic behaviors in relation to their structural defects. The results indicate that governed by the composition feature and microstructural defects, TiN/C nanocomposites exhibit not only distinct static magnetic properties but also exceptionally high dynamic permeability. Besides, TiN/C nanocomposites exhibit anomalously electromagnetic resonances, which means that there are some similar mechanisms between the permeability and permittivity. This is challenging for the traditional understanding of electromagnetism and makes it possible to achieve an appropriate balance between the permeability and permittivity simultaneously in a simple system. Particularly, sample T-900 has a lower magnetic moment but a higher dynamic permeability than T-1000, which is contradictive against classical physics theory in that a higher dynamic permeability refers to a higher magnetism and means there is no straightforward dependence between the weak static magnetic properties and the dynamic magnetic properties of TiN/C nanocomposites. This discovery gives a typical example to renew the unique electromagnetic characteristics of nanomaterials. Further theoretical and experimental efforts are also needed to better recognize the interactions between the electromagnetism and structural defects (the type and content of structural defects, or even their location and physical properties) of the title nanostructures and other non-magnetic nanostructures. This work, hopefully, is not only to provide some valuable clues to exploring the magnetism and absorbing mechanism of nanostructures but also to open up a novel and effective avenue to modulate the electromagnetic properties of MAM.
TiN/C nanocomposites were prepared with nanotubular titanic acid (H2Ti2O4(OH)2, denoted as NTA) and polyacrylamide (denoted as PAM) as the starting materials. Briefly, 1.90 g of NTA powder (the preparation of NTA is described elsewhere25) was dispersed in 50 mL of deionized water with the help of ultrasonic oscillation. Then 2.84 g of PAM was added into the solution and stirred vigorously until a uniform viscous dispersion was obtained. Resultant viscous dispersion was dried under vacuum at 80 °C to obtain a fluffy precursor (denoted as NTA/PAM). As-obtained NTA/PAM precursor was nitrided for 4 h at 400 °C, 700 °C, 900 °C and 1000 °C, respectively. Corresponding nitrided products are denoted as T-400, T-700, T-900 and T-1000, respectively. Moreover, TiN nanoparticles were also prepared for comparative studies under the same conditions while no carbon was introduced. Corresponding products without carbon, obtained by nitriding NTA at 900 °C for 4 h and 24 h, respectively, are denoted as T-4 and T-24.
The morphology of as-prepared products was examined with a transmission electron microscope (TEM, JEOL JEM-2010; accelerating voltage 200 kV) and a Philips X’Pert Pro X-ray diffractometer (XRD) was performed to analyze their phase structure (Cu-Kα radiation, λ = 1.5406 Å). Raman scattering spectra of as-prepared products were recorded with a RM-1000 facility (Renishaw; excitation source: 632.8 nm laser). Magnetic measurements were conducted with a superconducting quantum interference device (SQUID, MPMS XL-7, Quantum Design).
A proper amount of as-synthesized products was homogeneously dispersed in paraffin (paraffin as a binder is transparent for electromagnetic wave) at a mass fraction of 45:55 and then pressed into a toroidally-shaped sample with an inner diameter of 3.04 mm and an outer diameter of 7.00 mm for measurements of electromagnetic properties. The real and imaginary parts of the complex permittivity and permeability of resultant paraffin-based composites were measured in a frequency range of 2 ~ 18 GHz with an Agilent N5230A vector network analyzer. The reflection loss, RL (dB), is an effective evaluation standard of the microwave absorbance capacity of metal-backed slabs of material and low reflection corresponds to high absorption. It has been proven that the directly-measured and calculated RL are in remarkable agreement, due to the same underlying physical origin. To investigate the application potential of as-fabricated TiN/C composites, we also calculated their frequency dependence RL (dB) values according to the transmit-line theory by using the measured data of relative complex permeability and permittivity25.
How to cite this article: Gong, C. et al. Unique Static Magnetic and Dynamic Electromagnetic Behaviors in Titanium Nitride/Carbon Composites Driven by Defect Engineering. Sci. Rep. 6, 18927; doi: 10.1038/srep18927 (2016).
Alexandre, S. S., Lúcio, A. D., Castro Neto, A. H. & Nunes, R. W. Correlated magnetic states in extended one-dimensional defects in graphene. Nano Lett. 12, 5097–5102 (2012).
Article ADS CAS Google Scholar
Liu, F., Song, S. Y., Xue, D. F. & Zhang, H. J. Folded structured graphene paper for high performance electrode materials. Adv. Mater. 24, 1089–1094 (2012).
Guo, Y. Q., Xu, K., Wu, C. Z., Zhao, J. Y. & Xie, Y. Surface chemical-modification for engineering the intrinsic physical properties of inorganic two-dimensional nanomaterials. Chem. Soc. Rev. 44, 637–646 (2015).
Liu, J., Qiao, S. Z., Hu, Q. H. & Lu, G. Q. Magnetic nanocomposites with mesoporous structures: Synthesis and applications. Small 7, 425–443 (2011).
Cockayne, E., Rutter, G. M., Guisinger, N. P., Crain, J. N., First, P. N. & Stroscio, J. A. Grain boundary loops in graphene. Phys. Rev. B. 83, 195425 (2011).
Dev, P., Xue, Y. & Zhang, P. H. Defect-induced intrinsic magnetism in wide-gap III nitrides. Phys. Rev. Lett. 100, 117204 (2008).
Venkatesan, M., Fitzgerald, C. B. & Coey, J. M. D. Thin films: unexpected magnetism in a dielectric oxide. Nature. 430, 630–630 (2004).
Article ADS CAS Google Scholar
Pan, H. et al. Room-temperature ferromagnetism in carbon-doped ZnO. Phys. Rev. Lett. 99, 127201 (2007).
Article ADS CAS Google Scholar
Fitzgerald, C. B. et al. Magnetism in dilute magnetic oxide thin films based on SnO2 . Phys. Rev. B 74, 115307 (2006).
Das-Pemmaraju, C. & Sanvito, S. Ferromagnetism driven by intrinsic point defects in HfO2 . Phys. Rev. Lett. 94, 217205 (2005).
Hong, N. H., Sakai, J., Poirot, N. & Brizé, V. Room-temperature ferromagnetism observed in undoped semiconducting and insulating oxide thin films. Phys. Rev. B 73, 132404 (2006).
Tietze, T. et al. Interfacial dominated ferromagnetism in nanograined ZnO: a μSR and DFT study. Sci. Rep. 5, 8871 (2015).
Yoon, S. D. et al. Oxygen-defect-induced magnetism to 880 K in semiconducting anatase TiO2-δ films. J. Phys.: Condens. Matter. 18, 355–361 (2006).
Liu, Q. L., Zhang, D. & Fan, T. X. Electromagnetic wave absorption properties of porous carbon/Co nanocomposites. Appl. Phys. Lett. 93, 013110 (2008).
Zhang, X. F. et al. Microwave absorption properties of the carbon-coated nickel nanocapsules. Appl. Phys. Lett. 89, 053115 (2006).
Gong, C. H. et al. Synthesis of Ni/SiO2 nanocomposites for tunable electromagnetic absorption. Mater. Lett. 121, 81–84 (2014).
Meng, H. J. et al. Island-like nickel/carbon nanocomposites as potential microwave absorbers-Synthesis via in situ solid phase route and investigation of electromagnetic properties. J. Alloys. Compd. 644, 236–241 (2015).
Dong, J. Y. et al. Partially crystallized TiO2 for microwave absorption. J. Mater. Chem. A. 3, 5285–5288 (2015).
Xia, T., Zhang, C., Oyler, N. A. & Chen, X. B. Hydrogenated TiO2 nanocrystals: a novel microwave absorbing material. Adv. Mater. 25, 6905–6910 (2013).
Zhao, T. K. et al. Electromagnetic wave absorbing properties of amorphous carbon nanotubes. Sci. Rep. 4, 5619 (2014).
Snoek, J. L. Gyromagnetic resonance in ferrites. Nature 160, 90–90 (1947).
Article ADS CAS Google Scholar
Bai, X., Zhai, Y. & Zhang, H. Y. Green approach to prepare graphene-based composites with high microwave absorption capacity. J. Phys. Chem. C. 115, 11673–11677 (2011).
Chen, Y. H. et al. 3D Fe3O4 nanocrystals decorating carbon nanotubes to tune electromagnetic properties and enhance microwave absorption capacity. J. Mater. Chem. A. 3, 12621–12625 (2015).
Gong, C. H. et al. Room-temperature ferromagnetism evolution in nanostructured titanium nitride superconductors—the influence of structural defects. J. Mater. Chem. 21, 15273–15278 (2011).
Gong, C. H. et al. Synthesis and microwave electromagnetic properties of nanosized titanium nitride. J. Mater. Chem. 22, 3370–3376 (2012).
Yan, C. et al. Ferromagnetism and microwave electromagnetism of Iron-doped Titanium Nitride nanocrystals. J. Phys. Chem. C 116, 26006–26012 (2012).
Subramanian, B., Muraleedharan, C.V., Ananthakumar, R. & Jayachandran, M. A comparative study of titanium nitride (TiN), titanium oxy nitride (TiON) and titanium aluminum nitride (TiAlN), as surface coatings for bio implants. Surf. Coat. Technol. 205, 5014–5020 (2011).
Bernard, M., Deneuville, A., Thomas, O., Gergaud, P., Sandstrom, P. & Birch, J. Raman spectra of TiN/AlN superlattices. Thin Solid Films 380, 252–255 (2000).
Article ADS CAS Google Scholar
Senthilnathan, J. & Philip, L. Photocatalytic degradation of lindane under UV and visible light using N-doped TiO2 . Chem. Eng. J. 161, 83–92 (2010).
Zhang, X. F., Liu, Y. Y. & Qin, G. W. Break Snoek limit via superparamagnetic coupling in Fe3O4/silica multiple-core/shell nanoparticles. Appl. Phys. Lett. 106, 033105 (2015).
Vaz, F. et al. Influence of nitrogen content on the structural, mechanical and electrical properties of TiN thin films. Surf. Coat. Technol. 191, 317–323 (2005).
Zhan, Y. Q. Zhao, R., Lei, Y. J., Meng, F. B., Zhong, J. C. & Liu, X. B. A novel carbon nanotubes/Fe3O4 inorganic hybrid material: Synthesis, characterization and microwave electromagnetic properties. J. Magn. Magn. Mater. 323, 1006–1010 (2011).
Article ADS CAS Google Scholar
Huang, X. G., Zhang, J., Xiao, S. R., Sang, T. Y. & Chen, G. S. Unique electromagnetic properties of the zinc ferrite nanofiber. Mater. Lett. 124, 126–128 (2014).
Zhang, Y., Chai, C. P., Luo, Y. J., Wang, L. & Li, G. P. Synthesis, structure and electromagnetic properties of mesoporous Fe3O4 aerogels by sol-gel method. Mater. Sci. Eng. B 188, 13–19 (2014).
Liu, P. B., Huang, Y. & Sun, X. Excellent electromagnetic absorption properties of poly(3,4-ethylenedioxythiophene)-reduced graphene oxide-Co3O4 composites prepared by a hydrothermal method. ACS. Appl Mater. Inter. 5, 12355–12360 (2013).
Sundaresan, A. & Rao, C.N.R. Ferromagnetism as a universal feature of inorganic nanoparticles. Nano Today 4, 96–106 (2009).
Chen, S. C. et al. Microstructure and magnetic properties of oxidized titanium nitride thin films in situ grown by pulsed laser deposition. J. Phys. D: Appl. Phys. 46, 075002 (2013).
Song, N. N. et al. Exceeding natural resonance frequency limit of monodisperse Fe3O4 nanoparticles via superparamagnetic relaxation. Sci. Rep. 3, 3161 (2013).
This work was financially supported by the National Natural Science Foundation of China (grant Nos. 50902045, 20971037, 21271063 and 51471045), the Innovation Scientists and Technicians Troop Construction Projects of Henan Province (134100510005) and the Foundation for Youth Key Teachers of Henan Province (GGJS-024).
College of Chemistry and Chemical Engineering, Henan University, Kaifeng, 475004, P.R. China
Chunhong Gong, Hongjie Meng & Xiaowei Zhao
Engineering Research Center for Nanomaterials, Henan University, Kaifeng, 475004, P.R. China
Hongjie Meng, Laigui Yu, Jingwei Zhang & Zhijun Zhang
Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang, 110819, P.R. China
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
C.H. conceived the idea and J.W. designed the experiments. H.J. and X.W. participated in the fabrication and measurement of the samples. C.H., J.W. and X.F. performed the calculation and analyzed the data. C.H. and J.W. edited the manuscript and L.G. and Z.J. reviewed it. J.W. supervised this study and finalized the manuscript. All authors participated in data analysis.
The authors declare no competing financial interests.
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
Gong, C., Meng, H., Zhao, X. et al. Unique Static Magnetic and Dynamic Electromagnetic Behaviors in Titanium Nitride/Carbon Composites Driven by Defect Engineering. Sci Rep 6, 18927 (2016). https://doi.org/10.1038/srep18927
DOI: https://doi.org/10.1038/srep18927
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Journal of Materials Science: Materials in Electronics (2023)
Journal of Materials Science: Materials in Electronics (2023)
Journal of Materials Science: Materials in Electronics (2019)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
silver plated Cu Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.